HT-Mn75 Manganese agent
Product details
HT－Mn75 manganese agent
- Purpose:
Adjusting the content of manganese element in aluminum alloys of different grades to replace the master alloy can reduce the melting temperature.
- Product features:
- Element content 75%
- The actual recovery rate is greater than 95%
- Direct input, easy to use.
- How to use:
According to the content of alloying elements in the produced alloy grades and the analysis results before the furnace, calculate the required additive amount (Mn agent amount) according to the actual yield of 90%. After the small flame disappears, the manual stirring should be properly strengthened to make it diffuse evenly, and a certain diffusion time should be guaranteed according to the actual situation.
- Process parameters:
- Operating temperature: 740-760°C
- Addition amount (kg) = (alloy element composition (%) – pre-furnace analysis of the element content) ÷ actual yield (90%) × alloy element content in additives (70%) × furnace load (kg)
- Melting time: 15-30 minutes
- Packaging and storage:
| product name | model | use | Instructions | features | Process parameters | Specification |
| Titanium boron agent | HT-Ti4OB4 | Adjust the composition of alloying elements to replace the aluminum master alloy. | According to the content of alloying elements in the produced alloy grades and the results of furnace analysis, calculate the actual yield of 95%, the required amount of additives, after removing the slag, directly disperse and soak in the aluminum molten pool evenly, and wait for the small flame to disappear Finally, artificial stirring should be properly strengthened to make it diffuse evenly, and a certain diffusion time should be guaranteed according to the actual situation. | The element content is 75%, and the silicon content is 95%.
The actual yield is greater than 95%. The actual recovery rate of iron powder is greater than 90%. The shelf life is one year. |
Operating temperature: 740°C-760°C.
Melting time: 15-30 minutes. |
1. 500g/block
Density: 3.8-4.2kg/cm³ Si: 2.5g/cm³ |
| Titanium | HT-Ti75 | |||||
| Manganese | HT-Mn75 | |||||
| copper agent | HT-Cu75 | |||||
| Iron | HT-Fe75 | |||||
| Chromium agent | HT-Cr75 | |||||
| Nickel agent | HT-Ni75 | |||||
| Zinc agent | HT-Zn75 | |||||
| Fast Solvent | HT-Si95 |