HT-Cu75 Copper agent
Product details
- Purpose:
Adjust the content of copper element in different grades of aluminum alloy to replace the intermediate alloy, which can reduce the melting temperature.
- Product features:
- Element content 75%
- The actual recovery rate is greater than 95%
- Direct input, easy to use.
- How to use:
According to the content of alloying elements in the produced alloy grades and the results of furnace analysis, the required additives (Cu agent quantity) are calculated according to the 90% actual yield. After the flame disappears, manual stirring should be properly strengthened to make it diffuse evenly, and a certain diffusion time should be guaranteed according to the actual situation.
- Process parameters:
- Operating temperature: 740-760°C
- Addition amount (kg) = (alloy element composition (%) – pre-furnace analysis of the element content) ÷ actual yield (90%) × alloy element content in additives (70%) × furnace load (kg)
- Melting time: 15-30 minutes
- Packaging and storage:
25kg per box, stored in a dry place, the shelf life is six months.
| product name | model | use | Instructions | features | Process parameters | Specification |
| Titanium boron agent | HT-Ti4OB4 | Adjust the composition of alloying elements to replace the aluminum master alloy. | According to the content of alloying elements in the produced alloy grades and the results of furnace analysis, calculate the actual yield of 95%, the required amount of additives, after removing the slag, directly disperse and soak in the aluminum molten pool evenly, and wait for the small flame to disappear Finally, artificial stirring should be properly strengthened to make it diffuse evenly, and a certain diffusion time should be guaranteed according to the actual situation. | The element content is 75%, and the silicon content is 95%.
The actual yield is greater than 95%. The actual recovery rate of iron powder is greater than 90%. The shelf life is one year. |
Operating temperature: 740°C-760°C.
Melting time: 15-30 minutes. |
1. 500g/block
Density: 3.8-4.2kg/cm³ Si: 2.5g/cm³ |
| Titanium | HT-Ti75 | |||||
| Manganese | HT-Mn75 | |||||
| copper agent | HT-Cu75 | |||||
| Iron | HT-Fe75 | |||||
| Chromium agent | HT-Cr75 | |||||
| Nickel agent | HT-Ni75 | |||||
| Zinc agent | HT-Zn75 | |||||
| Fast Solvent | HT-Si95 |